Pickering emulsions are increasingly applied in drug delivery, oil-water separation, composite materials preparation, and other fields. However, systematic studies on the stabilization of Pickering emulsions to satisfy the growing application demands in multiple fields with long-term conservation are rare. Compared to conventional solid nanoparticles, polyanion-modified hairy nanoparticles are more stable in practical environments and are investigated in this study. Poly (sodium p-styrenesulfonate) was grafted to a polystyrene (PS) core via a photoemulsion polymerization. A hairy nanoparticle bearing polyanions called poly (sodium p-styrenesulfonate) brush (PS@PSS) was synthesized. The size and uniformity of the Pickering emulsions stabilized by PS@PSS were investigated via a polarizing microscope. The stability of Pickering emulsions were optimized by adjusting critical factors like ultrasonic power and time, standing time, oil phases, salt concentration, and water:oil ratio. Results indicated that the Pickering emulsions could be stabilized by PS@PSS nanoparticles, which showed remarkable and adjustable partial wetting properties. It was found that the optimized conditions were ultrasonic power of 150 W, ultrasonic time of 3 min, salt concentration of 0.1 mM, oil phase of hexadecane, and water:oil ratio of 1:1. The formation and stability of Pickering emulsion are closely related to the hairy poly (sodium p-styrenesulfonate) brush layer on the nanoparticle surface.
Keywords: hairy nanoparticles; photoemulsion polymerization; pickering emulsion.