Ultra-high molecular weight polyethylene (UHMWPE) and high-density polyethylene (HDPE) blend fibers with the highest tensile strength of 1.13 GPa were prepared by a melt spinning process. The mechanical behavior and crystal structure of the as-spun filaments and fibers were studied by differential scanning calorimetry (DSC), scanning electron microscopy (SEM), X-ray diffraction (XRD), sound velocity orientation testing, and tensile testing. The orientation degree, crystallinity, tensile strength, and initial modulus of the fibers increased with the increasing of the draw ratios. The grain size was shortened in the radial direction and elongated in the axial direction. The results suggested that the improvement of the tensile strength and initial modulus was a result of the compact crystal structure formed by slender grains composed of highly oriented molecular chains. Blending with HDPE could improve the formation of a slender and compact crystal structure, and the tensile strength and initial modulus of the blend fibers were higher.
Keywords: HDPE; UHMWPE; blend; fibers; melt spinning.