The synthesis and photoluminescence properties of crystal crosslinked gels (CCGs) with an aggregation-induced emission (AIE) active crosslinker derived from tetraphenylethene (TPE) is discussed in this article. The CCG was prepared from a metal organic framework (MOF) with large pore aperture to allow the penetration of TPE crosslinker. The obtained CCG possessed a rectangular shape originated from the parent MOF, KUMOF. The CCG showed stimuli-responsive photoluminescence behavior depending on the swelling degree, thus the photoluminescence intensity was higher at higher swelling degree. By changing the solvent, water content, or ionic strength, the photoluminescence intensity was controllable, accompanying the change of swelling degree. Moreover, emission color tuning was also achieved by the introduction of luminescent rare earth ions to form a coordination bonding with residual carboxylate inside the CCG.
Keywords: aggregation-induced emission (AIE); crystal crosslinking; metal-organic framework; polymer gel.