In this paper, a microscale high-frequency ultrasonic transducer was prepared by combining traditional planar ultrasonic phased-array technology and micro processing technology. The piezoelectric ceramic material PZT was used as the functional material of the transducer. The number of the arrays was 72, the width of each array was 50 μm, the pitch of each array was 70 μm, and the length of each array was 3 mm. The PZT chip was finely ground to a thickness of 130 μm and could reach a frequency of 10 MHz. The experimental platform of micron-scale precision was set up for a beam-forming lateral sound field test and imaging experiment to validate the theoretical analysis. The echo imaging test showed that a mold with a feature size of about 400 μm could be imaged well.
Keywords: PZT; beam forming; echo imaging; microscale; the micro processing technology; traditional planar ultrasonic phased array.