High aspect ratio silver nanowires (AgNWs) with ultra-long length and thin diameter were synthesized through bromine ion (Br-)-assisted one-step synthesis method. The bromine ions were used as pivotal passivating agent. When the molar ratio of Br-/Cl- was 1:4, the average diameter of AgNWs was as low as ~40 nm, the average length was as high as ~120 μm, and the aspect ratio reached 2500. Networks of AgNWs were fabricated using as-prepared high-quality AgNWs as conducting material and hydroxyethyl cellulose (HEC) as the adhesive polymer. As a result, a low sheet resistance down to ~3.5 Ω sq-1 was achieved with a concomitant transmittance of 88.20% and a haze of 4.12%. The ultra-low sheet resistance of conductive film was attributed to the long and thin AgNWs being able to form a more effective network. The adhesion of the AgNWs to the substrate was 0/5B (ISO/ASTM). The insights given in this paper provide the key guidelines for bromine ion-assisted synthesis of long and thin AgNWs, and further designing low-resistance AgNW-based conductive film for optoelectronic devices.
Keywords: Sheet resistance; Silver nanowires; Solvothermal; Transparent conductive film.