Enhanced surface decontamination of radioactive Cs by self-generated, strippable hydrogels based on reversible cross-linking

Abstract

A self-generated, strippable hydrogel containing adsorbents was developed to remove the radioactive cesium from surfaces by adsorption for wide-area surface decontamination. Two aqueous polymeric solutions of polyvinyl alcohol (PVA) and phenylboronic-acid-grafted alginate (PBA-Alg) were easily applied to surfaces and subsequently self-generated a hydrogel based on the PBA-diol ester bond. Compared to the strippable coating and chemical gels, the PBA-diol ester bond-based hydrogel was easily peeled off the surfaces without a drying step due to its high elasticity, which is more practical and time saving. The resulting hydrogel displayed high ¹³⁷Cs removal efficiencies of 91.61% for painted cement, 97.505% for aluminum, 94.05% for stainless steel, and 53.5% for cement, which was 2.3 times higher than that of Decongel due to the presence of the adsorbent in the hydrogel having an excellent Cs distribution coefficient (3.34 × 10⁴ mL/g). Moreover, the volume of radioactive waste generated after the surface decontamination could be reduced by a simple magnetic separation of the adsorbent from the used hydrogel, which can reduce the waste disposal cost. Therefore, our hydrogel system has great potential as a new, cost-effective surface decontaminant in various nuclear industry fields including wide-area environmental remediation after a nuclear accident or terrorist attack.

Keywords: Magnetic separation; Phenylboronic acid-diol ester bond; Radioactive cesium; Strippable hydrogel; Surface decontamination.