Degradable, flame retardant, and flexible nanocomposite films with low dielectric constant were prepared with poly (lactic acid) (PLA), nano ZIF-8@GO, and degradable flame-retardant resorcinol di(phenyl phosphate) (RDP). The SEM results of the fractured surfaces indicated that ZIF-8@GO and RDP were dispersed uniformly in the PLA matrix. The prepared films had good mechanical properties and the tensile strength of the film with 1.5 wt% of ZIF-8@GO was increased to 48.2 MPa, compared with 38.5 MPa of pure PLA. Meanwhile, the nanocomposite films were flexible due to the toughing effect of RDP. Moreover, above 27.0% of limited oxygen index (LOI) and a VTM-0 rating were achieved for the nanocomposite films. The effects of nano ZIF-8@GO hybrids and RDP on the dielectric properties were investigated, and the results showed that ZIF-8@GO and RDP were beneficial in reducing the dielectric constant and dielectric loss of the nanocomposites.
Keywords: PLA; ZIF-8@GO hybrids; dielectric constant; flame-retardant; flexible.