In recent years, organo-halide perovskite solar cells have garnered a surge of interest due to their high performance and low-cost fabrication processing. Owing to the multilayer architecture of perovskite solar cells, interface not only has a pivotal role to play in performance, but also influences long-term stability. Here we have employed diverse morphologies of electron selective layer (ESL) to elucidate charge extraction behavior in perovskite solar cells. The TiO₂ mesoporous structure (three-dimensional) having varied thickness, and nanocolumns (1-dimensional) with tunable length were employed. We found that a TiO₂ electron selective layer with thickness of about c.a. 100 nm, irrespective of its microstructure, was optimal for efficient charge extraction. Furthermore, by employing impedance spectroscopy at different excitation wavelengths, we studied the nature of recombination and its dependence on the charge generation profile, and results showed that, irrespective of the wavelength region, the fresh devices do not possess any preferential recombination site, and recombination process is governed by the bulk of the perovskite layer. Moreover, depending on the type of ESL, a different recombination mechanism was observed that influences the final behavior of the devices.
Keywords: charge dynamics; electron transport material; metal-halides perovskites; titanium oxide.