A trilayer SiO₂/Ag/SiO₂ nanocap array was prepared on a two-dimensional template. When annealed at different temperatures, the curvature of the SiO₂/Ag/SiO₂ nanocap arrays increased, which led to Ag nanocap shrinkage. The stress provided by the curved SiO₂ layer induced the formation of Ag nanotwins. Ag nanotwins assisted the growth of nanoparticles when the neighboring nanotwins changed the local misorientations. Nanocap shrinkage reduced the surface plasmon resonance (SPR) coupling between neighboring nanocaps; concurrently, grain growth decreased the SPR coupling between the particles in each nanocap, which led to a red shift of the localized surface plasmon resonance (LSPR) bands and decreased the surface-enhanced Raman scattering (SERS) signals.
Keywords: SERS; SiO2/Ag/SiO2 nanocap arrays; grains growth.