In hyper-stoichiometric uranium oxide, both neutron diffraction work and, more recently, theoretical analyses report the existence of clusters such as the 2:2:2 cluster, comprising two anion vacancies and two types of anion interstitials. However, little is known about whether there exists a region of low deviation-from-stoichiometry in which defects remain isolated, or indeed whether at high deviation-from-stoichiometry defect clusters prevail that contain more excess oxygen atoms than the di-interstitial cluster. In this study, we report pair distribution function (PDF) analyses of UO2 and UO2+ x ( x ≈ 0.007 and x ≈ 0.16) samples obtained from high-temperature in situ neutron scattering experiments. PDF refinement for the lower deviation from stoichiometry sample suggests the system is too dilute to differentiate between isolated defects and di-interstitial clusters. For the UO2.16 sample, several defect structures are tested, and it is found that the data are best represented assuming the presence of center-occupied cuboctahedra.