Silk fibroin isolated from Bombyx mori cocoons is a promising material for a range of biomedical applications, but it has no inherent cell-interactive domains, necessitating functionalization with bioactive molecules. Here we demonstrate significantly enhanced cell interactions with silk fibroin biomaterials in the absence of biofunctionalization following surface modification using plasma immersion ion implantation (PIII). Further, PIII treated silk fibroin biomaterials supported direct covalent immobilization of proteins on the material surface in the absence of chemical cross-linkers. Surface analysis after nitrogen plasma and PIII treatment at 20 kV revealed that the silk macromolecules are significantly fragmented, and at the higher fluences of implanted ions, surface carbonization was observed to depths corresponding to that of the ion penetration. Consistent with the activity of radicals created in the treated surface layer, oxidation was observed on contact with atmospheric oxygen and the PIII treated surfaces were capable of direct covalent immobilization of bioactive macromolecules. Changes in thickness, amide and nitrile groups, refractive index, and extinction coefficient in the wavelength range 400-1000 nm as a function of ion fluence are presented. Reactions responsible for the restructuring of the silk surface under ion beam treatment that facilitate covalent binding of proteins and a significant improvement in cell interactions on the modified surface are proposed.
Keywords: biomaterial; cell interactions; covalent biofunctionalization; plasma immersion ion implantation; silk.