Polyetheretherketone (PEEK) is a popular polymeric biomaterial which is primarily used as an intervertebral spacer in spinal fusion surgery; but it is developed for trauma, prosthodontics, maxillofacial, and cranial implants. It has the purported advantages of an elastic modulus which is similar to native bone and it can be easily formed into custom 3D shapes. Nevertheless, PEEK's disadvantages include its poor antibacterial resistance, lack of bioactivity, and radiographic transparency. This study presents a simple approach to correcting these three shortcomings while preserving the base polymer's biocompatibility, chemical stability, and elastic modulus. The proposed strategy consists of preparing a PEEK composite by dispersing a minor fraction (i.e., 15 vol%) of a silicon nitride (Si3 N4 ) powder within its matrix. In vitro tests of PEEK composites with three Si3 N4 variants-β-Si3 N4 , α-Si3 N4 , and β-SiYAlON-demonstrate significant improvements in the polymer's osteoconductive versus SaOS-2 cells and bacteriostatic properties versus gram-positive Staphylococcus epidermidis bacteria. These properties are clearly a consequence of adding the bioceramic dispersoids, according to chemistry similar to that previously demonstrated for bulk Si3 N4 ceramics in terms of osteogenic behavior (vs both osteosarcoma and mesenchymal progenitor cells) and antibacterial properties (vs both gram-positive and gram-negative bacteria).
Keywords: antibacterial; composite; osteoconductive; polyetheretherketone; silicon nitride.
© 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.