In order to enhance the photoreduction of CO2 to CH4, a new type of photocatalyst, Sb1.5Sn8.5-xTixO19.0, with high conductivity and low bandgap was developed by partially incorporating Ti into the framework of Sb1.5Sn8.5O19.0 (antimony-doped tin oxide, ATO) using a controlled hydrothermal method. XRD and TEM analyses indicated that the Sb1.5Sn8.5-xTixO19.0 particles exhibited a tetragonal crystal structure and were approximately 20 nm in size. Furthermore, the bandgap and conductivity of these materials increased with increasing Ti content. A study of the photoreduction of CO2 with H2O revealed a remarkable increase in the generation of CH4 over the Sb1.5Sn8.5-xTixO19.0 catalysts. In particular, CH4 generation was the highest when Sb1.5Sn8.5Ti1.0O19.0 was used as the photocatalyst, and was three-fold higher than that achieved by using anatase TiO2. Photoluminescence studies showed that the enhanced photocatalytic activity of the Sb1.5Sn8.5-xTixO19.0 materials could be attributed to the interfacial transfer of photogenerated charges, which led to an effective charge separation and inhibition of the recombination of photogenerated electron-hole (e-/h+) pairs.