The surface plays an exceptionally important role in nanoscale materials, exerting a strong influence on their properties. Consequently, even a very thin coating can greatly improve the optoelectronic properties of nanostructures by modifying the light absorption and spatial distribution of charge carriers. To use these advantages, 1D/1D heterostructures of ZnO/WS2 core/shell nanowires with a-few-layers-thick WS2 shell were fabricated. These heterostructures were thoroughly characterized by scanning and transmission electron microscopy, X-ray diffraction, and Raman spectroscopy. Then, a single-nanowire photoresistive device was assembled by mechanically positioning ZnO/WS2 core/shell nanowires onto gold electrodes inside a scanning electron microscope. The results show that a few layers of WS2 significantly enhance the photosensitivity in the short wavelength range and drastically (almost 2 orders of magnitude) improve the photoresponse time of pure ZnO nanowires. The fast response time of ZnO/WS2 core/shell nanowire was explained by electrons and holes sinking from ZnO nanowire into WS2 shell, which serves as a charge carrier channel in the ZnO/WS2 heterostructure. First-principles calculations suggest that the interface layer i-WS2, bridging ZnO nanowire surface and WS2 shell, might play a role of energy barrier, preventing the backward diffusion of charge carriers into ZnO nanowire.
Keywords: 1D/1D heterostructures; core/shell nanowires; photodetectors; transitional metal chalcogenides; van der Waals epitaxy.