Adsorption or immobilization of proteins on synthetic surfaces is a key issue in the context of the biocompatibility of implant materials, especially those intended for the needs of cardiac surgery but also for the construction of biosensors or nanomaterials used as drug carriers. The subject of research was the analysis of Raman spectra of two types of fibrous carbon nanomaterials, of great potential for biomedical applications, incubated with human serum albumin (HSA). The first nanomaterial has been created on the layer of MWCNTs deposited by electrophoretic method (EPD) and then covered by thin film of pyrolytic carbon introduced by chemical vapor deposition process (CVD). The second material was formed from carbonized nanofibers prepared via electrospinning (ESCNFs) of polyacrylonitrile (PAN) precursor and then covered with pyrolytic carbon (CVD). The G-band blue-shift towards the position of about 1600cm-1, observed for both studied surfaces, clearly indicates the albumin (HSA) adhesion to the surface. The G and G' (2D) peak shift was employed to assess the stress build up on the carbon nanomaterials. The surface nano- and micro-topography as well as the method of ordering the carbon nanomaterial has a significant influence on the mode of surface-protein interaction.
Keywords: Carbon nano fibers (CNFs); Carbon nanomaterials; Human serum albumin (HSA); Multi-walled carbon nanotubes (MWCNTs); Pyrolytic carbon C (CVD); Raman microspectroscopy.
Copyright © 2018 Elsevier B.V. All rights reserved.