The surface activated bonding (SAB) method generally has the advantage of high bonding strength, low contact resistance, and high microstructural stability at room temperature. In this study, Ti-Al laminates were produced by surface activated bonding with aluminum and titanium foils. Heat treatment was conducted at the temperature range from 200 to 550 °C in vacuum. The bonding strength Ti-Al laminates was measured by a peel test, and the interfacial characteristics were investigated microstructural observation. The results showed that the bonding strength was the highest with heat treatment at 400 °C, microstructure observation revealed that the bonding strength of the Ti-Al laminate was influenced by the interfacial characteristics.