A novel polyethoxysilsesquiazane ([EtOSi(NH)1.5]n, EtOSZ) was synthesized by ammonolysis at -78 °C of ethoxytrichlorosilane (EtOSiCl₃), which was isolated by distillation as a reaction product of SiCl₄ and EtOH. Attenuated total reflection-infra red (ATR-IR), 13C-, and 29Si-nuclear magnetic resonance (NMR) spectroscopic analyses of the ammonolysis product resulted in the detection of Si-NH-Si linkage and EtO group. The simultaneous thermogravimetric and mass spectrometry analyses of the EtOSZ under helium revealed cleavage of oxygen-carbon bond of the EtO group to evolve ethylene as a main gaseous species formed in-situ, which lead to the formation at 800 °C of quaternary amorphous Si-C-N with an extremely low carbon content (1.1 wt %) when compared to the theoretical EtOSZ (25.1 wt %). Subsequent heat treatment up to 1400 °C in N₂ lead to the formation of X-ray amorphous ternary Si-O-N. Further heating to 1600 °C in N₂ promoted crystallization and phase partitioning to afford Si₂N₂O nanocrystallites identified by the XRD and TEM analyses. The thermal stability up to 1400 °C of the amorphous state achieved for the ternary Si-O-N was further studied by chemical composition analysis, as well as X-ray photoelectron spectroscopy (XPS) and 29Si-NMR spectroscopic analyses, and the results were discussed aiming to develop a novel polymeric precursor for ternary amorphous Si-O-N ceramics with an enhanced thermal stability.
Keywords: Polymer-Derived Ceramics (PDCs); amorphous state; silicon oxynitride; thermal stability.