We investigated scintillation properties of organic-inorganic layered perovskite-type compounds under gamma-ray and X-ray irradiation. A crystal of the hybrid compounds with phenethyl amine (17 × 23 × 4 mm) was successfully fabricated by the poor-solvent diffusion method. The bulk sample showed superior scintillation properties with notably high light yield (14,000 photons per MeV) under gamma-rays and very fast decay time (11 ns). The light yield was about 1.4 time higher than that of common inorganic material (GSO:Ce) confirmed under 137Cs and 57Co gamma-rays. In fact, the scintillation light yield was the highest among the organic-inorganic hybrid scintillators. Moreover, it is suggested that the light yield of the crystal was proportional with the gamma-ray energy across 122-662 keV. In addition, the scintillation from the crystal had a lifetime of 11 ns which was much faster than that of GSO:Ce (48 ns) under X-ray irradiation. These results suggest that organic-inorganic layered perovskite-type compounds are promising scintillator for gamma-ray detection.