A general strategy for synthesizing high-coercivity L10-FePt nanoparticles

Wenjuan Lei; Yongsheng Yu; Weiwei Yang; Ming Feng; Haibo Li

doi:10.1039/c7nr04849a

A general strategy for synthesizing high-coercivity L1₀-FePt nanoparticles

Nanoscale. 2017 Sep 14;9(35):12855-12861. doi: 10.1039/c7nr04849a.

Authors

Wenjuan Lei¹, Yongsheng Yu, Weiwei Yang, Ming Feng, Haibo Li

Affiliation

¹ MIIT Key Laboratory of Critical Materials Technology for New Energy Conversion and Storage, School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin, Heilongjiang 150001, China. ysyu@hit.edu.cn yangww@hit.edu.cn.

PMID: 28849847
DOI: 10.1039/c7nr04849a

Abstract

It is extremely desirable but challenging to develop a facile solution phase synthesis to directly prepare well-dispersed L1₀-FePt nanoparticles (NPs) to meet the requirements of advanced magnets in modern industry and information technology. Here, we report a novel strategy to synthesize hard magnetic L1₀-FePt NPs via controlled co-reduction of Fe(acac)₃ and K₂PtCl₆ in the presence of oleylamine, in which effective control of the magnetic properties and chemical ordering of L1₀-FePt NPs was achieved by tuning the mole ratio of the precursors, reaction time and temperature. The highest coercivity of 10.5 kOe can be obtained for the NPs synthesized at 350 °C for 8 h, which is much higher than the coercivities reported by the previous studies on solution-synthesized FePt NPs without annealing or the third elemental additive. The reported one-pot synthesis of L1₀-FePt NPs may provide an ideal class of building blocks for magnetic energy applications.