Objective: To analyze the risk factors for laser fiber fractures when deflected to form a curve, including laser settings, size of the laser fiber, and the fiber bending diameter.
Materials and methods: Single-use 272 and 365 μm fibers (Rocamed®, Monaco) were employed along with a holmium laser (Rocamed). Five different fiber curve diameters were tested: 9, 12, 15, 18, and 20 mm. Fragmentation and dusting settings were used at a theoretical power of 7.5 W. The laser was activated for 5 minutes and the principal judgment criterion was fiber fracture. Every test for each parameter, bending diameter, and fiber size combinations was repeated 10 times.
Results: With dusting settings, fibers broke more frequently at a curved diameter of 9 mm for both 272 and 365 μm fibers (p = 0.037 and 0.006, respectively). Using fragmentation settings, fibers broke more frequently at 12 mm for 272 μm and 15 mm for 365 μm (p = 0.007 and 0.033, respectively). Short pulse and high energy were significant risk factors for fiber fracture using the 365 μm fibers (p = 0.02), but not for the 272 μm fibers (p = 0.35). Frequency was not a risk factor for fiber rupture. Fiber diameters also seemed to be involved in the failure with a higher number of broken fibers for the 365 μm fibers, but this was not statistically significant when compared with the 272 μm fibers (p > 0.05).
Conclusion: Small-core fibers are more resistant than large-core fibers as lower bending diameters (<9 mm) are required to break smaller fibers. In acute angles, the use of small-core fibers, at a low energy and long-pulse (dusting) setting, will reduce the risk of fiber rupture.
Keywords: deflection; fiber; laser; lower pole lithotripsy; uretersocopy; urolithiasis.