Thermal mismatch strain induced disorder of Y2Mo3O12 and its effect on thermal expansion of Y2Mo3O12/Al composites

Chang Zhou; Qiang Zhang; Saiyue Liu; Bingcheng Luo; Eongyu Yi; Enke Tian; Guowu Li; Longtu Li; Gaohui Wu

doi:10.1039/c7cp00676d

Thermal mismatch strain induced disorder of Y₂Mo₃O₁₂ and its effect on thermal expansion of Y₂Mo₃O₁₂/Al composites

Phys Chem Chem Phys. 2017 May 17;19(19):11778-11785. doi: 10.1039/c7cp00676d.

Authors

Chang Zhou¹, Qiang Zhang, Saiyue Liu, Bingcheng Luo, Eongyu Yi, Enke Tian, Guowu Li, Longtu Li, Gaohui Wu

Affiliation

¹ School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, People's Republic of China. zhang_tsiang@hit.edu.cn wugh@hit.edu.cn.

PMID: 28435967
DOI: 10.1039/c7cp00676d

Abstract

Fully dense Y₂Mo₃O₁₂/Al composites were prepared by squeeze-casting. Relatively mild conditions of 750 °C/20 min/50 MPa were used in order to avoid reaction of the components. SEM, Raman spectroscopy, XRD and dilatometry were used to characterize the microstructures and morphologies of the composites. Zero thermal expansion was achieved in the temperature range where the thermal mismatch strain was zero. We show that the CTE mismatch of Al and Y₂Mo₃O₁₂ results in compressive and tensile strains that distort the Y₂Mo₃O₁₂ lattice. We establish a novel method to measure the negative thermal expansion (NTE) materials' CTE under strain by measuring the composites' CTE and calculating the thermal mismatch strain between the NTE ceramic and the metal matrix. The relationship between thermal strain and Raman shift is established and measured and the simulated results are in good agreement. We also find Y₂Mo₃O₁₂ to have a positive CTE when the surface strain is ≥0.80 × 10^-2%.