Synthesis of Pt3Y and Other Early-Late Intermetallic Nanoparticles by Way of a Molten Reducing Agent

Abstract

Early-late intermetallic phases have garnered increased attention recently for their catalytic properties. To achieve the high surface areas needed for industrially relevant applications, these phases must be synthesized as nanoparticles in a scalable fashion. Herein, Pt₃Y-targeted as a prototypical example of an early-late intermetallic-has been synthesized as nanoparticles approximately 5-20 nm in diameter via a solution process and characterized by XRD, TEM, EDS, and XPS. The key development is the use of a molten borohydride (MEt₃BH, M = Na, K) as both the reducing agent and reaction medium. Readily available halide precursors of the two metals are used. Accordingly, no organic ligands are necessary, as the resulting halide salt byproduct prevents sintering, which further permits dispersion of the nanoscale intermetallic onto a support. The versatility of this approach was validated by the synthesis of other intermetallic phases such as Pt₃Sc, Pt₃Lu, Pt₂Na, and Au₂Y.