In this work, maghemite intercalated montmorillonite (γFe₂O₃-MMT)/polymer nanocomposites loaded with 1 or 2 wt.% of nanofillers were obtained by photopolymerization of difunctional acrylate monomers. The γFe₂O₃-MMT nanofillers were prepared by a new method based on the in situ formation of maghemite in the interlayer space of Fe-MMT using a three step process. X-ray diffraction (XRD), chemical analysis, TG/DTA and transmission electron microscopy (TEM) characterization of these nanofillers indicated the efficiency of the synthesis. When following the kinetics of the photopolymerization of diacrylate-γFe₂O₃-MMT nanocomposites using FTIR spectroscopy no significant inhibition effect of the nanofillers was observed at a loading up to 2 wt.%. These innovative nanocomposites exhibit improved mechanical properties compared to the crude polymer.
Keywords: ion exchange; maghemite; montmorillonite; nanocomposites; photopolymerization.