Self-assembly of silver nanoparticles as high active surface-enhanced Raman scattering substrate for rapid and trace analysis of uranyl(VI) ions

Shaofei Wang; Jiaolai Jiang; Haoxi Wu; Jianping Jia; Lang Shao; Hao Tang; Yiming Ren; Mingfu Chu; Xiaolin Wang

doi:10.1016/j.saa.2017.02.042

Self-assembly of silver nanoparticles as high active surface-enhanced Raman scattering substrate for rapid and trace analysis of uranyl(VI) ions

Spectrochim Acta A Mol Biomol Spectrosc. 2017 Jun 5:180:23-28. doi: 10.1016/j.saa.2017.02.042. Epub 2017 Feb 22.

Authors

Shaofei Wang¹, Jiaolai Jiang¹, Haoxi Wu¹, Jianping Jia¹, Lang Shao¹, Hao Tang¹, Yiming Ren¹, Mingfu Chu¹, Xiaolin Wang²

Affiliations

¹ Institute of Materials, China Academy of Engineering Physics, PO Box 9071-11, Mianyang 621907, China.
² China Academy of Engineering Physics, Mianyang 621900, China. Electronic address: xlwang@caep.cn.

PMID: 28262580
DOI: 10.1016/j.saa.2017.02.042

Abstract

A facile surface-enhanced Raman scattering (SERS) substrate based on the self-assembly of silver nanoparticles on the modified silicon wafer was obtained, and for the first time, an advanced SERS analysis method basing on this as-prepared substrate was established for high sensitive and rapid detection of uranyl ions. Due to the weakened bond strength of OUO resulting from two kinds of adsorption of uranyl species ("strong" and "weak" adsorption) on the substrate, the ν₁ symmetric stretch vibration frequency of OUO shifted from 871cm^-1 (normal Raman) to 720cm^-1 and 826cm^-1 (SERS) along with significant Raman enhancement. Effects of the hydrolysis of uranyl ions on SERS were also investigated, and the SERS band at ~826cm^-1 was first used to approximately define the constitution of uranyl species at trace quantity level. Besides, the SERS intensity was proportional to the variable concentrations of uranyl nitrate ranging from 10^-7 to 10^-3molL^-1 with an excellent linear relation (R²=0.998), and the detection limit was ~10^-7molL^-1. Furthermore, the related SERS approach involves low-cost substrate fabrication, rapid and trace analysis simultaneously, and shows great potential applications for the field assays of uranyl ions in the nuclear fuel cycle and environmental monitoring.

Keywords: Adsorption mechanism; SERS; Self-assembly; Trace analysis; Uranyl(VI).