This in vitro investigation of the behavior of two types of calcium phosphate glass ceramics on the basis of phosphates of biogenic or synthetic origin prepared from initial mixtures with different particle size has revealed that some different factors affect the behavior, namely the phase composition of composite, fraction of open porosity, and average diameter of pore channels. It was established that the solubility of the composites on the basis of synthetic calcium phosphates and glass after 2 and 7 days contact with saline composites is the highest among the materials under study. First of all, this fact is related to the peculiarities of their phase composition, high fraction of open porosity, and high permeability. As for biogenic hydroxyapatite/glass materials, their solubility is several times lower in spite of close total porosity. The particle size of initial mixture practically does not affect the material solubility; the latter is only slightly lower for smaller particles.
Keywords: Calcium phosphate; Composite; Glass; Hydroxyapatite; In vitro; Porosity; Solubility.