Continuously porous hydroxyapatite (HAp)/t-ZrO2 composites containing concentric laminated frames and microchanneled bodies were fabricated by an extrusion process. To investigate the mechanical properties of HAp/t-ZrO2 composites, the porous composites were sintered at different temperatures using a microwave furnace. The microstructure was designed to imitate that of natural bone, particularly small bone, with both cortical and spongy bone sections. Each microchannel was separated by alternating lamina of HAp, HAp-(t-ZrO2) and t-ZrO2. HAp and ZrO2 phases existed on the surface of the microchannel and the core zone to increase the biocompatibility and mechanical properties of the HAp-ZrO2 artificial bone. The sintering behavior was evaluated and the optimum sintering temperature was found to be 1400 °C, which produced a stable scaffold. The material characteristics, such as the microstructure, crystal structure and compressive strength, were evaluated in detail for different sintering temperatures. A detailed in vitro study was carried out using MTT assay, western blot analysis, gene expression by polymerase chain reaction and laser confocal image analysis of cell proliferation. The results confirmed that HAp-ZrO2 performs as an artificial bone, showing excellent cell growth, attachment and proliferation behavior using osteoblast-like MG63 cells.
Keywords: 10.01; 10.03; bioceramic; cortical bone; extrusion; hydroxyapatite (HAp); osteoblast cell.