The photoluminescence (PL) and PL excitation (PLE) spectra of Si6-z Al z O z N8-z (β-sialon):Eu2+ phosphors with small z values (z=0.025-0.24) were studied at room temperature and 6 K. The PL and PLE spectra exhibit fine structure with the PL lines being as sharp as 45-55 nm even at room temperature; this fine structure was enhanced by decreasing the z value. These results can be used for expanding the color gamut of liquid crystal displays, particularly in the blue-green region. From low-temperature measurements, the fine PLE structure was ascribed to discrete energy levels of 7FJ states. The 4f65d excited states of Eu2+ are considered to be localized near the 4f orbital. This is because the bonding of Eu2+ with surrounding atoms is ionic rather than covalent. Lattice phonon absorptions were also observed in the PLE spectrum, revealing that the optically active Eu2+ ions are located in the β-sialon crystal. The PL spectrum of the sample with the smallest z value (0.025) consists of a sharp zero-phonon line and lattice phonon replicas, which results in a sharp and asymmetric spectral shape.
Keywords: LCD; LED; phosphor; photoluminescence; sialon.