The need to improve electrodes and Li-ion conducting materials for rechargeable all-solid-state batteries has drawn enhanced attention to the investigation of lithium-rich compounds. The study of the ternary system Li-Si-P revealed a series of new compounds, two of which, Li8 SiP4 and Li2 SiP2 , are presented. Both phases represent members of a new family of Li ion conductors that display Li ion conductivity in the range from 1.15(7)×10-6 Scm-1 at 0 °C to 1.2(2)×10-4 Scm-1 at 75 °C (Li8 SiP4 ) and from 6.1(7)×10-8 Scm-1 at 0 °C to 6(1)×10-6 Scm-1 at 75 °C (Li2 SiP2 ), as determined by impedance measurements. Temperature-dependent solid-state 7 Li NMR spectroscopy revealed low activation energies of about 36 kJ mol-1 for Li8 SiP4 and about 47 kJ mol-1 for Li2 SiP2 . Both compounds were structurally characterized by X-ray diffraction analysis (single crystal and powder methods) and by 7 Li, 29 Si, and 31 P MAS NMR spectroscopy. Both phases consist of tetrahedral SiP4 anions and Li counterions. Li8 SiP4 contains isolated SiP4 units surrounded by Li atoms, while Li2 SiP2 comprises a three-dimensional network based on corner-sharing SiP4 tetrahedra, with the Li ions located in cavities and channels.
Keywords: ionic conductors; lithium; phosphorus; silicon; ternary phases.
© 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.