Al-50Si alloys were joined by rapid ultrasound-induced transient-liquid-phase bonding method using Zn foil as interlayer at 390°C in air, below the melt point of interlayer. The fracture of oxide films along the edge of Si particles led to contact and inter-diffusion between aluminum substrate and Zn interlayer, and liquefied Zn-Al alloys were developed. The width of Zn-Al alloys gradually decreased with increasing the ultrasonic vibration time due to liquid squeezing out and accelerated diffusion. A stage of isothermal solidification existed, and the completion time was significantly shortened. In the liquid metal, the acoustic streaming and ultrasonic cavitations were induced. As the process developed, much more Si particles, which were particulate-reinforced phases of Al-50Si, gradually migrated to the center of soldering seam. The highest average shear strength of joints reached to 94.2MPa, and the fracture mainly occurred at the base metal.
Keywords: Joining; Mechanical properties; Microstructures; Particle-reinforcement; Ultrasound.
Copyright © 2016 Elsevier B.V. All rights reserved.