In steels the dependence of ambient temperature microstructure and mechanical properties on solidification rate is not well reported. In this work we investigate the microstructure and hardness evolution for a low C low Mn NbTi-microalloyed steel solidified in the cooling rate range of 1-50 Cs-1. The maximum strength was obtained at the intermediate solidification rate of 30 Cs-1. This result has been correlated to the microstructure variation with solidification rate.