Kesterite, a highly promising photo-absorbing crystalline form of Cu2ZnSnS4 (CZTS), has been prepared via various routes. However, the lack of in-depth understanding of the dynamic phase formation process of kesterite leads to difficulties in optimizing its annealing conditions, hence its light harvesting performance. In this paper, in situ Raman monitored-annealing is applied to study the phase formation kinetics of nano-crystalline kesterite from a precursor deposited on a TiO2 mesoscopic scaffold. By performing in situ Raman annealing under different experimental conditions and wavelengths, several facts have been discovered: kesterite crystallization starts at as low as 170 °C, but after short time annealing at 300 °C followed by cooling, the initially formed kesterite is found to decompose. Annealing at 400 °C or higher is proven to be sufficient for stabilizing the kesterite phase. Annealing at the higher temperature of 500 °C is necessary though to promote a complete reaction and thus eliminate the parasitic copper tin sulfide (CTS) impurity intermediates identified at lower annealing temperatures. More importantly, the real-time temperature dependence of Raman peak intensity enhancement, shift and broadening for CZTS is established experimentally at 500 °C for 1 h, providing a valuable reference in future CZTS research. This work demonstrates the significance of using in situ Raman spectroscopy in elucidating the kesterite phase formation kinetics, a critical step towards full crystal phase control - a prerequisite for developing fully functional CZTS-based optoelectronic devices.