Surface-enhanced Raman scattering (SERS) and surface-enhanced photoluminescence (SEPL) are emerging as versatile widespread methods for biological, chemical, and physical characterization in close proximity of nanostructured surfaces of plasmonic materials. Meanwhile, single-step, facile, cheap, and green technologies for large-scale fabrication of efficient SERS or SEPL substrates, routinely demonstrating both broad plasmonic response and high enhancement characteristics, are still missing. In this research, single-pulse spallative micron-size craters in a thick Ag film with their internal nanotexture in the form of nanosized tips are for the first time shown to demonstrate strong polarization-dependent enhancement of SEPL and SERS responses from a nanometer-thick covering Rhodamine 6G layer with average enhancement factors of 40 and 2 × 10(6), respectively. Additionally, the first detailed experimental study is reported for physical processes, underlying the formation mechanisms of ablative nanotextures on such "thick" metal films. Such mechanisms demonstrate a complex "hybrid" fluence-dependent ablation character-appearance of spallative craters, typical for bulk material, at low fluences and formation of upright standing nanotips (frozen nanojets), usually associated with thin-film ablation, in the crater centers at higher fluences. Moreover, special emphasis was made on the possibility to reshape the nanotopography of such spallative craters through multipulse laser-induced merging of their small nanotips into larger ones. The presented approach holds promise to be one of the cheapest and easiest-to-implement ways to mass-fabricate various efficient spallation-nanotextured single-element plasmonic substrates for routine chemo- and biosensing, using MHz-repetition-rate femtosecond fiber laser sources with multiplexed laser-beams.
Keywords: femtosecond pulses; nanotopography reshaping; red−green−blue color analysis; spallative crater; surface-enhanced Raman scattering; surface-enhanced photoluminescence.