Defect depth profiles of Cu (In1-x,Gax)(Se1-ySy)2 (CIGSS) were measured as functions of pulse width and voltage via deep-level transient spectroscopy (DLTS). Four defects were observed, i.e., electron traps of ~0.2 eV at 140 K (E1 trap) and 0.47 eV at 300 K (E2 trap) and hole traps of ~0.1 eV at 100 K (H1 trap) and ~0.4 eV at 250 K (H2 trap). The open circuit voltage (VOC) deteriorated when the trap densities of E2 were increased. The energy band diagrams of CIGSS were also obtained using Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS), and DLTS data. These results showed that the valence band was lowered at higher S content. In addition, it was found that the E2 defect influenced the VOC and could be interpreted as an extended defect. Defect depth profile images provided clear insight into the identification of defect state and density as a function of depth around the space charge region.