Mn3O4@CoMn2O4 nanoparticles (NPs) were produced at low temperature and ambient atmosphere using a one-pot two-step synthesis protocol involving the cation exchange of Mn by Co in preformed Mn3O4 NPs. Selecting the proper cobalt precursor, the nucleation of CoxOy crystallites at the Mn3O4@CoMn2O4 surface could be simultaneously promoted to form Mn3O4@CoMn2O4-CoxOy NPs. Such heterostructured NPs were investigated for oxygen reduction and evolution reactions (ORR, OER) in alkaline solution. Mn3O4@CoMn2O4-CoxOy NPs with [Co]/[Mn] = 1 showed low overpotentials of 0.31 V at -3 mA·cm(-2) and a small Tafel slope of 52 mV·dec(-1) for ORR, and overpotentials of 0.31 V at 10 mA·cm(-2) and a Tafel slope of 81 mV·dec(-1) for OER, thus outperforming commercial Pt-, IrO2-based and previously reported transition metal oxides. This cation-exchange-based synthesis protocol opens up a new approach to design novel heterostructured NPs as efficient nonprecious metal bifunctional oxygen catalysts.
Keywords: OER; ORR; cation exchange; cobalt oxide; colloidal; electrocatalysis; manganese oxide; nanoparticle.