This paper investigated the mackinawite (FeS)-associated products formed during reaction between FeS and carbon tetrachloride (CT) at pH 7 and 8. At pH 8, reaction of FeS with CT led to formation of abundant spherical particles with diameters between 50 and 400 nm on the FeS surface and in solution; far fewer such particles were observed at pH 7. Analysis of the FeS surface by energy dispersive X-ray spectroscopy after reaction with CT at pH 8 showed decreased sulfur and elevated oxygen compared to unreacted FeS. The spherical particles that formed upon FeS reaction with CT were mostly amorphous with localized areas of poorly crystalline two-line ferrihydrite. X-ray photoelectron spectroscopy indicated that the predominant Fe surface species after reaction with CT at pH 8 was Fe(III)-O, consistent with ferrihydrite and other amorphous iron (hydr)oxides as major products. Powder X-ray diffraction analysis suggested formation of greigite upon reaction of FeS with CT at pH 7. Both ferrihydrite and Fe(2+), which is a product of greigite dissolution, can react with dissolved HS(-) to form FeS, suggesting that, after oxidation by chlorinated aliphatics, FeS can be regenerated by addition or microbial generation of sulfide.