Fast responsive macroporous interpenetrating polymer network (IPN) hydrogels were fabricated in this work by a sequential strategy, as follows: the first network, consisting of poly(N,N-dimethylaminoethyl methacrylate) (PDMAEM) cross-linked with N,N'-methylenebisacrylamide (BAAm), was prepared at -18 °C, the second network consisting of poly(acrylamide) (PAAm) cross-linked with BAAm, being also generated by cryogelation technique. Both single network cryogels (SNC) and IPN cryogels were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, and water uptake. The presence of weak polycation PDMAEM endows the SNCs and the IPNs cryogels with sensitivity at numerous external stimuli such as pH, temperature, ionic strength, electric field, among which the first three were investigated in this work. It was found that the initial concentration of monomers in both networks was the key factor in tailoring the properties of IPN cryogels such as swelling kinetics, equilibrium water content (EWC), phase transition temperature and the response at ionic strength. The pore size increased after the formation of the second network, the swelling kinetics in pure water being comparable with that of the SNC, phase transition temperature being situated in the range 35-36 °C for IPN cryogels. The water uptake at equilibrium (WUeq) abruptly increased at pH < 3.0 in the case of SNCs, whereas the response of IPN cryogels at the decrease of pH from 6.0 to 1.0 was strongly dependent on the gel structure, the values of WUeq being lower at a higher concentration of DMAEM in the first network, the monomer concentration in the second network being about 10 wt %. The pH response was very much diminished when the monomer concentration was high in both networks (15 wt % in the first network, and 21 wt % in the second network). The increase of the ionic strength from 0 up to 0.3 M NaCl led to the decrease of the WUeq, for all cryogels, the level of dehydration being higher and faster for the SNC than for the corresponding IPN cryogel. The release of diclofenac sodium (DS), as a model acidic drug, triggered by pH, temperature, and ionic strength from the IPN cryogels was evaluated. A pulsatile release of DS from the IPN cryogels was presented, with a slower release at 34 °C (below VPTT) and a faster release at 37 and 40 °C (above the VPTT).
Keywords: N,N-dimethylaminoethyl methacrylate; controlled drug delivery; interpenetrating polymer network; multiresponsive cryogel; swelling.