The characteristics of nanoparticles (NPs) uptake may fundamentally alter physicochemical effects of engineered NPs on aquatic organisms, thereby yielding different ecotoxicology assessment results. The adsorption behavior of nano-TiO2 (P-25) on zebrafish embryos in Holtfreter's medium (pH 7.2, I ∼ 7.2 × 10(-2) M) and the presence of sodium alginate (100 mg/L) as dispersant was investigated. Zebrafish embryos (total 100) were exposed to nano-TiO2 at different concentrations (e.g., 0, 10, 20, 60, 120 mg/L) in batch-mode assay. The adsorption capacity of nano-TiO2 on fish eggs was determined by measuring the Ti concentration on the egg surface using ICP-OES analysis. Results showed that the adsorption capacity increased rapidly in the first hour, and then declined to reach equilibrium in 8 h. The adsorption characteristics was visualized as a three-step process of rapid initial layer formation, followed by break-up of aggregates and finally rearrangement of floc structures; the maximum adsorption capacity was the sum of an inner rigid layers of aggregates of 0.81-0.84 μg-TiO2/#-egg and an outer softly flocculated layers of 1.01 μg-TiO2/#-egg. The Gibbs free energy was 543.29-551.26 and 100.75 kJ/mol, respectively, for the inner-layer and the outer-layer aggregates. Adsorption capacity at 0.5-1.0 μg-TiO2/#-egg promoted egg hatching; but hatching was inhibited at higher adsorption capacity. Results clearly showed that the configuration of TiO2 aggregates could impact the hatching efficiency of zebrafish embryos.
Keywords: Adsorption; Embryos; Flocculation; Hatching; TiO(2); Zebrafish.
Copyright © 2016 Elsevier Ltd. All rights reserved.