We investigated the tribological properties of diamond-like carbon (DLC) films prepared with TiC interlayer of various thicknesses as the adhesive layer. DLC and TiC thin films were prepared using unbalanced magnetron (UBM) sputtering method using graphite and titanium as targets. TiC films as the interlayer were deposited under DLC films and various physical, tribological, and structural properties of the films fabricated with various TiC interlayer thicknesses were investigated. With various TiC interlayer thicknesses under DLC films, the tribological properties of films were improved with increasing thickness and the DLC/TiC layer fabricated by unbalanced magnetron sputtering method are exhibited maximum high hardness over 27 GPa and high elastic modulus over 242 GPa, and a smooth surface below 0.09 nm.