We report the development of hydroxyapatite nanoparticle (HAp NP)-functionalized hetero-graft materials (HGMs) for dental applications. These HGMs were prepared by attaching platelet-, needle-, and sphere-shaped HAp NPs to the surface of xenograft materials through chemical conjugation. Although all three HAp NPs contributed to increase the surface area of bone graft material (BGM), the shape of the HAp NPs was a determining factor. Platelet HAp NPs were most effective, because they caused a 48.9% increase in BGM surface area whereas the influence of the spherical NP was only a 6.7% increase. This suggests that geometric factors regarding both the attached HAp NPs and graft material surface are essential in controlling the surface roughness of graft materials. Among the three HAp NPs, it was the platelet HAp NPs that helped to increase the efficacy of the BGM most significantly. Compared with BGM with no HAp NP attachment, HGM with platelet HAp NP ('platelet-HGM) treatment had ~46.1% higher cell attachment and proliferation rate. The MTT assay also showed that the HAp NP-treated hetero-graft materials had negligible cytotoxicity.