This study aims to compare stress transmitted to implants and passive fit of one-piece cast frameworks fabricated with 3 different materials: commercially pure titanium (G1-CP Ti), cobalt-chromium alloy (G2-Co-Cr), and nickel-chromium-titanium alloy (G3-Ni-Cr-Ti). In total, 12 frameworks simulating bars for fixed prosthesis in a model with 5 implants were fabricated. The passive fit of the framework interface was measured using an optical microscope and the stresses transmitted to implants were measured using quantitative photoelastic analysis. Data were statistically analyzed by analysis of variance (ANOVA) and least significant difference (LSD) tests (α = 0.05). Mean and standard deviation values of passive fit and stress over implants are presented, respectively: G1 [472.49 (109.88) μm and 11.38 (9.23) KPa], G2 [584.84 (120.20) μm and 15.83 (9.30) KPa], and G3 [462.70 (179.18) μm and 16.39 (9.51) KPa]. For stress over implants, there were significant differences between G1, G2, and G3 (P = 0.035), being the lowest values for the G1. There were no significant differences for passive fit between G1 and G3 (P = 0.844), but both were statistically different from G2 (P = 0.028 and P = 0.035, respectively), which showed the worse results. It may be concluded that the stress over implants was affected by the tested materials. The CP Ti presented the best values for the evaluated items.