Green synthesis of silver nanoparticles (AgNPs) using Hybanthus enneaspermus extract at room temperature that act as a reducing agent as well as capping agent has been investigated. The synthesized AgNPs were characterized by UV-visible spectroscopy, X-ray diffraction (XRD), Fourier transform infrared (FTIR), zeta potential, and dynamic light scattering (DLS) transmission electron microscopy (TEM) and energy-dispersive X-ray (EDX). The silver surface plasmon resonance was observed at 420 nm in the UV-visible spectrum. XRD peaks were observed at 2θ values in 38.20°, 44.40°, 64.60°, and 77.50° which are indexed as (111), (200), (220), and (311) bands of face-centered cubic (fcc) structures of silver. FTIR revealed the AgNPs were capped with plant compounds of alcohol, phenols, carbonyl, amines, and amide functional groups. TEM image shows that the particles were of spherical, hexagonal, and triangular in shape, and the size range was 16-26 nm. Further, DLS exhibits the average size of 25.2 nm and the zeta values were measured (-27.1 mV) which proves the stability of the AgNPs. The conversion of Ag(+) ions into Ag(0) was calculated using inductively coupled plasma atomic emission spectroscopy (ICP-MS) and was found to be 96 %. The biosynthesized AgNPs showed the larvicidal activity with the LC50 values of 17.24 and 13.12 mg/L against the fourth-instar larvae of Anopheles subpictus and Culex quinquefasciatus, respectively. The GC-MS analysis of the plant extract showed that 39 bioactive phytochemical compounds have been found to possess a wide range of activities, which may help in the protection against incurable diseases.
Keywords: Hybanthus enneaspermus; Larvicidal activity; Silver nanoparticles; Zeta potential.