The property development of the ethylene-tetrafluoroethylene copolymer (ETFE) membrane induced by simultaneous biaxial drawing was investigated. Commonly, tensile strength can be increased by drawing; conversely, tear resistance decreases. In this study, the balance between tensile strength and tear resistance for the resultant ETFE membrane was optimized achieved by a combination of lamination of low molecular weight (LMW) and high molecular weight (HMW) layers and subsequent biaxial drawing. The structural factor determining tear resistance of these biaxially drawn membranes was determined based on in situ small-angle X-ray scattering (SAXS) measurement during tensile deformation simulating tearing tests. Lozenge shaped scattering, which indicated inclined lamellae, was observed during such tensile deformation of the resultant membranes. Remarkably, this inclined lamellar structure was observed for the pure LMW membrane; however, it also appeared at the interface between LMW and HMW layers within biaxially drawn membranes. For the membrane exhibiting the highest tearing strength, the fraction of such inclined lamella increased up to the critical strain corresponding to the actual sample breaking. These results confirm that the inclined lamellar structure absorbed strain during membrane tearing.