In this work we study brazing of Al2O3 to Ti with biocompatibility properties, using a Au-foil as joining element. Al2O3 was produced by sintering of powder at 1550°C. Al2O3 samples were coated with a 2 and 4μm thick of Mo layer and then stacked with Ti. Al2O3-Mo/Au/Ti combinations were joined at 1100°C in vacuum. Successful joining of Mo-Al2O3 to Ti was observed. Interface shows the formation of a homogeneous diffusion zone. Mo diffused inside Au forming a concentration line. Ti3Au and TiAu phases were observed.
Keywords: Alumina; Brazing; Metal/ceramic joining; Titanium.