We report the demonstration of continue wave operation of diode end-pumped Er:Y2O3 and Er:Lu2O3 ceramic lasers operating at 2.7 μm at room temperature. The maximum output power of 320 mW and 611 mW was obtained from the Er:Y2O3 and Er:Lu2O3 ceramic lasers, with slope efficiency of 6.5% and 7.6%, respectively. Characteristics of Red-shift in lasing wavelength of the ceramic lasers was investigated and discussed. The study indicates that under 967 nm and 976 nm LD pumping, 15 at.% Er-doped Lu2O3 ceramic exhibit a better performance than that of Y2O3 at room temperature.