The purpose of this study was to evaluate the genotoxic potential of components leached from two conventional self-curing glass-ionomer cements (Fuji IX and Ketac Molar), and light-curing, resin modified glass-ionomer cements (Vitrebond, Fuji II LC). Evaluation was performed on human lymphocytes using alkaline and hOGG1 modified comet, and micronucleus assays. Each material, polymerised and unpolymerised, was eluted in extracellular saline (1 cm2 mL-1) for 1 h, 1 day, and 5 days. Cultures were treated with eluates using final dilutions of 10(-2), 10(-3), and 10(-4). Alkaline comet assay did not detect changes in DNA migration of treated cells regardless of the ionomer tested, polymerisation state, and elution duration. Glass ionomers failed to significantly influence micronucleus frequency. No oxidative DNA damage in treated lymphocytes was observed using hOGG1 modified comet assay. Obtained results indicate high biocompatibility of all tested materials used in the study under experimental conditions.