Ultrasonic cavitation erosion of gas nitrided Ti-6Al-4V alloys

I Mitelea; E Dimian; I Bordeaşu; C Crăciunescu

doi:10.1016/j.ultsonch.2014.01.005

Ultrasonic cavitation erosion of gas nitrided Ti-6Al-4V alloys

Ultrason Sonochem. 2014 Jul;21(4):1544-8. doi: 10.1016/j.ultsonch.2014.01.005. Epub 2014 Jan 13.

Authors

I Mitelea¹, E Dimian², I Bordeaşu³, C Crăciunescu⁴

Affiliations

¹ "Politehnica" University of Timisoara, Department of Materials and Manufacturing Engineering, Bd. Mihai Viteazul 1, 300026 Timisoara, Romania. Electronic address: imitelea@mec.upt.ro.
² "Politehnica" University of Timisoara, Department of Materials and Manufacturing Engineering, Bd. Mihai Viteazul 1, 300026 Timisoara, Romania. Electronic address: e.dimian@mec.upt.ro.
³ "Politehnica" University of Timisoara, Department of Mechanical Machines, Equipments and Transportation, Bd. Mihai Viteazul 1, 300026 Timisoara, Romania. Electronic address: ilarica59@gmail.com.
⁴ "Politehnica" University of Timisoara, Department of Materials and Manufacturing Engineering, Bd. Mihai Viteazul 1, 300026 Timisoara, Romania. Electronic address: craciunescucm@yahoo.com.

PMID: 24500067
DOI: 10.1016/j.ultsonch.2014.01.005

Abstract

Ultrasonic cavitation erosion experiments were performed on Ti-6Al-4V alloys samples in annealed, nitrided and nitrided and subsequently heat treated state. The protective oxide layer formed as a result of annealing and heat treatment after nitriding is eliminated after less than 30 min cavitation time, while the nitride layer lasts up to 90 min cavitation time. Once the protective layer is removed, the cavitation process develops by grain boundary erosion, leading to the expulsion of grains from the surface. The gas nitrided Ti-6Al-4V alloy, forming a TixN surface layer, proved to be a better solution to improve the cavitation erosion resistance, compared to the annealed and nitrided and heat treated state, respectively. The analysis of the mean depth of erosion rate at 165 min cavitation time showed an improvement of the cavitation erosion resistance of the nitrided samples of up to 77% higher compared to the one of the annealed samples.

Keywords: Cavitation; Erosion; Nitriding; Oxidation; Surface; Ti-alloys.