The neutral, distorted octahedral complex [TiCl4(Se n Bu2)2] (1), prepared from the reaction of TiCl4 with the neutral Se n Bu2 in a 1:2 ratio and characterized by IR and multinuclear (1H, 13C{1H}, 77Se{1H}) NMR spectroscopy and microanalysis, serves as an efficient single-source precursor for low-pressure chemical vapor deposition (LPCVD) of titanium diselenide, TiSe2, films onto SiO2 and TiN substrates. X-ray diffraction patterns on the deposited films are consistent with single-phase, hexagonal 1T-TiSe2 (P3̅m1), with evidence of some preferred orientation of the crystallites in thicker films. The composition and structural morphology was confirmed by scanning electron microscopy (SEM), energy dispersive X-ray, and Raman spectroscopy. SEM imaging shows hexagonal plate crystallites growing perpendicular to the substrate, but these tend to align parallel to the surface when the quantity of reagent is reduced. The resistivity of the crystalline TiSe2 films is 3.36 ± 0.05 × 10-3 Ω·cm with a carrier density of 1 × 1022 cm-3. Very highly selective film growth from the reagent was observed onto photolithographically patterned substrates, with film growth strongly preferred onto the conducting TiN surfaces of SiO2/TiN patterned substrates. TiSe2 is selectively deposited within the smallest 2 μm diameter TiN holes of the patterned TiN/SiO2 substrates. The variation in crystallite size with different diameter holes is determined by microfocus X-ray diffraction and SEM, revealing that the dimensions increase with the hole size, but that the thickness of the crystals stops increasing above ∼20 μm hole size, whereas their lengths/widths continue to increase.
Keywords: Selective deposition; chemical vapor deposition; microfocus X-ray diffraction; selenoether; single-source precursor; titanium selenide.