In this study, we have investigated temporal evolution of silicon surface topography under 500-eV argon ion bombardment for two angles of incidence, namely 70° and 72.5°. For both angles, parallel-mode ripples are observed at low fluences (up to 2 × 1017 ions cm-2) which undergo a transition to faceted structures at a higher fluence of 5 × 1017 ions cm-2. Facet coarsening takes place at further higher fluences. This transition from ripples to faceted structures is attributed to the shadowing effect due to a height difference between peaks and valleys of the ripples. The observed facet coarsening is attributed to a mechanism based on reflection of primary ions from the facets. In addition, the role of sputtering is investigated (for both the angles) by computing the fractional change in sputtering yield and the evolution of surface roughness. PACS: 81.05.Cy, 81.16.Rf, 61.80.Jh, 87.64.Dz.