High-quality blue-green emitting ZnxCd(1-x)S(1-y)Se(y)/ZnS core/shell quantum dots (QDs) have been synthesized by a phosphine-free method. The quantum yields of as-synthesized ZnxCd(1-x)S(1-y)Se(y)/ZnS core/shell QDs can reach 50-75% with emissions between 450 and 550 nm. The emissions of such core/shell QDs are not susceptible to ligand loss through the photostability test. Blue-green light-emitting diodes (LEDs) based on the low-cadmium ZnxCd(1-x)S(1-y)Se(y)/ZnS core/shell QDs have been successfully demonstrated. Composite films of poly[9,9-dioctylfluorene-co-N-[4-(3-methylpropyl)]-diphenylamine] (TFB) and ZnO nanoparticle layers were chosen as the hole-transporting and the electron-transporting layers, respectively. Highly bright blue-green QD-based light-emitting devices (QD-LEDs) showing maximum luminance up to 10000 cd/m(2), in particular, the blue QD-LEDs show an unprecedentedly high brightness over 4700 cd/m(2) and peak external quantum efficiency (EQE) of 0.8%, which is the highest value ever reported. These results signify a remarkable progress in QD-LEDs and offer a practicable platform for the realization of QD-based blue-green display and lighting.