Gold (Au)-embedded indium tin oxide (ITO) nanowires were synthesized by thermal evaporation of a mixture of In(2)O(3,) SnO(2) and graphite powders on Si (100) substrates coated with Au thin films followed by annealing. At the initial stages of annealing, Au formed a continuous linear core located along the long axis of each ITO nanowire. The morphology of the Au core changed from a continuous line to a discrete line, and then to a droplet-like chain, finally evolving into a peapod in which crystalline Au nanoparticles were encapsulated in crystalline ITO with increasing annealing temperature. The ITO nanowires with the Au core showed an emission band at ~380 nm in the ultraviolet region. The ultraviolet emission intensity increased rapidly with increasing annealing temperature. The intensity of emission from the Au-peapod ITO nanowires (annealed at 750 °C) was approximately 20 times higher than that of the emission from the Au-core/ITO-shell ITO nanowires with a continuous linear shaped-Au core (annealed at 550 °C). This ultraintense ultraviolet emission might have originated mainly from the enhanced crystalline quality of the annealed ITO nanowires.
© 2011 American Chemical Society